Adhesive for FC board to phenolic foam

Adhesive for FC board to phenolic foam
Adhesive for phenolic foam to FC board
Glue for FC board to phenolic foam
Glue for phenolic foam to FC board
Adhesive for FC fiber cement board to phenolic foam
Glue for FC fiber cement board to phenolic foam
Adhesive for phenolic foam to FC fiber cement board
Adhesive for FC fiber cement wall panel
Adhesive for FC fiber cement exterior decorative wall panel

Use to make wall insulation board

Suitable product :

PU-50 Double-component type Polyurethane Glue

1. Range of application
Pu-50 double-component type polyurethane glue has been extensively used as an adhesive between aluminum honeycomb and aluminum plate, between EPS FWB or XPS, which included in light building materials or wall insulation board, and calcium silicate board or steel plate or aluminum plate or processed stone or grade of outer wallmarble , stone aluminum honeycomb panels .
2. Physical & Chemical Properties
Pu-50 type polyurethane glue, as a type of solvent-free, non-benzene and nonformaldehyde glue, is superior in waterproof, cold resistance and weatherability with its fine thixotropy and high cohesional strength. It also characterizes its non-foam and solidifying under normal temperature.

Item Unit Index
1 Appearance Component A:white viscous fluid
Component B:dark brown liquid
2 Viscosity Pa.s component A:≤25.0
component B:≤2.5
3 Quantity of solids ≥98
4 Specific density g/cm 1.20±0.11
5 Tensile strength under normal temperature(23C±1C) Mpa Metal to Metal≥10 Metal plate/aluminum
aluminum honeycomb
6 Tensile strength under low temperature(-137C±2C) Metal to Metal≥12
7 dissolution of Media Not dissolved in Styrofoam
8 Application life min <15

3. Usage Methods
(1) Remove oil, dust, rust staining and water.
(2) Make sure that the mixture weight ratio of component A and component B is 5:1. Then pour the mixture into a wide mouth barrel and stir it quickly with an electric agitator .Homogeneously spread the glue on cohered surface with sawtooth scrapers. The glue can also be mixed on cohered surface of metal plate directly with scraping plates.
(3)Dose of the applied glue should be controlled between 150g/m and 300 g/m according to cohered surfaces. It is recommended to increase the dose on the surface of aluminum honeycomb plates.
(4) When operated in mechanical roller painting, the glue should be mixed in batches to avoid solidifying on rubber roller.
(5)When glue spread on, cover adhering material by raising pressure for solidification.
(6)Solidification process can be operated under normal temperature or heating for higher cohesional strength(reference data:80℃/20min).
4. Caution
(1) Application life of the glue is about 15 minutes(less time if under high temperature) from stirring under normal temperature.
(2) For more time to application, it is recommended to mix directly two components on cohered surface or pour the mixture immediately from barrel.
(3) In order to get the tack of glue, keep the surface with glue on air for 15 minutes.
Above technical tips are only for suggestions. Users should work out their techniques according to tests.
5. Storage and Package
Storage :One year when stored free of solarization and frost under normal temperature.
Package:Component A: 25kg/plastic barrel of wide mouth Component B: 25kg/plastic barrel

If any technology questions, please call us +0086 13422583570 (

Product Tags:

phenolic foam panels


phenolic foam panel


phenolic foam insulation

China Adhesive for FC board to phenolic foam

Adhesive for FC board to phenolic foam Images

Inquiry Cart 0
Send your message to this supplier
Characters Remaining: (0/3000)
Inquiry Cart 0