Self-leveling Low-viscosity Fast-Turnaround Surface Repair Material

Country/Region china
Company Zhejiang Taizheng Construction Material Co., Ltd
Categories High Speed Spindle Repair
Telephone +86-571-87569602
ICP License Issued by the Chinese Ministry
  • Haven't found right suppliers
  • Our buyer assistants can help you find the most suitable, 100% reliable suppliers from China.
  • And this service is free of charge.
  • we have buyer assistants who speak English, French, Spanish......and we are ready to help you anytime!
  • Submit Buying Request
    • Product Details
    • Company Profile

    Self-leveling Low-viscosity Fast-Turnaround Surface Repair Material

    Product Details


    TasirRapid Surface Repair Easy Mix is a self-leveling, low viscosity, two-part liquid polyurethane-hybrid polymer. When supplemented with its proprietary blended aggregate, this product is used to repair and rehabilitate concrete and asphaltic concrete pavements. The enhanced polymer is high performance, rapid setting, and can be used to make an impact and traffic resistant polymer concrete that can be used at temperatures down to 0°F (-18°C). Within minutes of placement, durable, long-lasting repairs are able to handle vibration, heavy traffic, and thermal movement.


    No priming required to bond to concrete, asphalt, steel or wood

    Waterproof, chemically resistant membrane protects substrates from freeze-thaw spalling

    Use neat or with aggregate

    Stops further corrosion of reinforcing steel

    Traffic ready in as little as 30 minutes*

    Very low odor

    Make repairs year roundcan be used in temperatures down to 0°F (-18°C)


    Expansion joint and bridge header reconstruction

    Control joint filler

    Repair cracks, potholes, spalls

    Airport runways, walkways, floors, and parking lots

    Airport lighting cans and conduit channels


    Tasir Rapid Surface Repair Easy Mix is packaged in a.64 gal. (2.42 L) kit containing. 32 gal. (1.21 L) A”, .32 gal. (1.21 L) B” and 50 lbs.

    (22.7 kg) of aggregate yielding approximately.41 ft3 (.011 m3) per kit.


    One year in original unopened packaging when stored in dry conditions; high relative humidity and temperature will reduce shelf life.

    *Traffic time dependent upon air and substrate temperature.


    Mix Ratio by Volume

    (1) Part A: (1) Part B

    Viscosity @ 77°F (25°C) - mixed

    60 cps

    Gel Time, Neat

    2 to 3 minutes

    Working time with Aggregate

    Approx. 5 minutes



    Dark Grey

    Cure Time (reopen to traffic)

    30 minutes

    Hardness, Durometer D, ASTM D-2240


    Tensile Strength, ASTM D-412

    3,000 psi (20.7 MPa)

    Compressive Strength, ASTM C-579B

    1 hour

    2,000 psi (13.8 MPa)

    1 day

    6,000 psi (41.3 MPa)

    7 days

    7,000 psi (48.2 MPa)

    28 days

    8,000 psi (55.1 MPa)

    Elongation, ASTM D-638

    10 - 15%

    Bond Strength, ASTM C-882

    2,000 psi (13.8 MPa)


    1. Prepare concrete surfaces to a minimum CSP-4 (Concrete Surface Profile per ICRI Technical Standard 03732). Ensure surfaces are clean, sound and rough prior to repair.

    2. For overlays, cut keyway channel (groove) using concrete saw equipped with dry cut diamond blade around perimeter of area to be resurfaced. Keyway channel (groove) depth shall be a minimum of 1/2 inch (12.7 mm). Surfaces adjacent to a vertical plane (such as curbs, walls, tanks, etc.) shall have keyway channels cut approximately 4 6 inches (101.6 - 152.3 mm) back from vertical plane towards the interior of area to be resurfaced. Keyway channel shall be 1/2 inch (12.7 mm) deep by 1/2 inch (12.7 mm) wide.

    3. For overlays, chip 2 inch (50.8 mm) wide taper back from interior edge of keyway channel at all termination edges (i.e., drains, doors, etc.). Using bush hammer or chipping gun equipped with a 1 2 inch (24.4 - 50.8 mm) wide spade blade, chip a 2 inch (50.8 mm) wide taper back from edge of interior keyway channel (groove) inward towards the area being resurfaced. Taper shall match depth of keyway channel at its deepest point, which is the edge of the keyway, and taper out to 0 inches at its most shallow point, 2 inches (50.8 mm) towards the interior of the area to be resurfaced.

    4. For crack filling, route out as necessary to a maximum 1/2 inch wide by 1/2 inch deep, minimum.

    5. Vacuum dust and dirt from all surfaces.

    6. Surfaces must be completely dry and free of moisture prior to installation.

    MIXING INSTRUCTIONS: Mix ratio is 1:1 by volume. Mix a small sample and test prior to actual placement. Larger mix volumes can generate

    Product Tags:

    rubber gloves


    product packaging

    Quality Self-leveling Low-viscosity Fast-Turnaround Surface Repair Material for sale
    Send your message to this supplier
    To: Zhejiang Taizheng Construction Material Co., Ltd
    Characters Remaining: (0/3000)
    Inquiry Cart 0

    Home| Products| Suppliers| Quality Suppliers| Site Map |About Us |Contact Us |Help |关于我们 |联系我们

    Copyright © 2009 - 2019 All rights reserved.